Comparación de la resistencia compresiva entre diferentes tipos de ionómeros de vidrio

dc.creatorHernández Rivera, Alejandra
dc.date2014-04-23
dc.date.accessioned2016-05-02T22:19:10Z
dc.date.available2016-05-02T22:19:10Z
dc.identifierhttp://revistas.ucr.ac.cr/index.php/Odontos/article/view/14322
dc.identifier.urihttps://hdl.handle.net/10669/21372
dc.descriptionThe purpose of this article was to compare the compressive strength of different glass ionomers. 30 samples were made, divided into groups of 10. Ketac Easy Mix, Vitremer and Ketac N 100, were used for the test. Cylinders were made of each material, following the manufacturer’s instructions for each case, using molds Ultradent preformed for this purpose. The samples were stored in water at 37 ° C for 24 hrs, before being faulted in an Olsen testing machine Tiinus H 10 Ks at a speed of 0.1 cm / min. The Ketac Easy Mix had a compressive strength of 40.9 Mpa, the Vitremer had an average strength of 111.7 MPa, whereas for Ketac N 100 was 117.4 MPa. Hybrids glass ionomers have a higher compression resistance, far superior to conventional glass ionomer evaluated.es-ES
dc.descriptionThe purpose of this article was to compare the compressive strength of different glass ionomers. 30 samples were made, divided into groups of 10. Ketac Easy Mix, Vitremer and Ketac N 100, were used for the test. Cylinders were made of each material, following the manufacturer’s instructions for each case, using molds Ultradent preformed for this purpose. The samples were stored in water at 37 ° C for 24 hrs, before being faulted in an Olsen testing machine Tiinus H 10 Ks at a speed of 0.1 cm / min. The Ketac Easy Mix had a compressive strength of 40.9 Mpa, the Vitremer had an average strength of 111.7 MPa, whereas for Ketac N 100 was 117.4 MPa. Hybrids glass ionomers have a higher compression resistance, far superior to conventional glass ionomer evaluated en-US
dc.formatapplication/pdf
dc.languagespa
dc.publisherUniversidad de Costa Ricaen-US
dc.rightsCopyright (c) 2014 Odovtosen-US
dc.sourceOdovtos International Journal of Dental Sciences; Οδοντος (Odontos): Número 14; 55-58es-ES
dc.sourceOdovtos - International Journal of Dental Sciences; Οδοντος (Odontos): Número 14; 55-58en-US
dc.source2215-3411
dc.source1659-1046
dc.source10.15517/ijds.v0i14
dc.subjectglass ionomeres-ES
dc.subjectcompressive strengthes-ES
dc.titleComparación de la resistencia compresiva entre diferentes tipos de ionómeros de vidrioes-ES
dc.titleComparación de la resistencia compresiva entre diferentes tipos de ionómeros de vidrioen-US
dc.typeartículo original


Ficheros en el ítem

FicherosTamañoFormatoVer

No hay ficheros asociados a este ítem.

Este ítem aparece en la(s) siguiente(s) colección(ones)

Mostrar el registro sencillo del ítem